Керамический диэлектрический конденсатор ВЧ/СВЧ со сверхнизким ESR

Керамический диэлектрический конденсатор ВЧ/СВЧ со сверхнизким ESR

Получить цену

Количество минимального заказа:

Свяжитесь

Описание продукта

Атрибуты продукта

Упаковка и доставка

Описание продукта

Атрибуты продукта

Модель: DLC75N(0201)

Упаковка и доставка

The file is encrypted. Please fill in the following information to continue accessing it

Описание продукта

DLC75N — это радиочастотный MLCC со сверхнизким ESR и высокой добротностью.

DLC75N Ультранизкое ESR, ВЧ/СВЧ керамический диэлектрический конденсатор

DLC75N(0201)

Таблица емкости DLC75N

Capacitance (pF)	Code	Tolerance	Rated Voltage	Capacitance (pF)	Code	Tolerance	Rated Voltage	Capacitance (pF)	Code	Tolerance	Rated Voltage
0.2	0R2	A, B, C, D.	25V Code 250	1.7	1R7	A, B, C, D.	25V Code 250	6.2	6R2	B, C,	25V Code 250
0.3	0R3			1.8	1R8			6.8	6R8
0.4	0R4			1.9	1R9			7.5	7R5
0.5	0R5			2.0	2R0			8.2	8R2
0.6	0R6			2.1	2R1			9.1	9R1
0.7	0R7			2.2	2R2			10	100	F, G, J.
0.8	0R8			2.4	2R4			11	110
0.9	0R9			2.7	2R7			12	120
1.0	1R0			3.0	3R0			13	130
1.1	1R1			3.3	3R3			15	150
1.2	1R2			3.6	3R6			16	160
1.3	1R3			3.9	3R9			18	180
1.4	1R4			4.3	4R3
1.5	1R5			4.7	4R7
1.6	1R6			5.1	5R1
				5.6	5R6

Номер компонента

Тип и размер торцевой крышки DLC75N

Электрические характеристики

Item	Specification
Quality Factor (Q)	≥ 2000, measured at 1 ± 0.1 MHz, 1 ± 0.2 Vrms.
Insulation Resistance (IR)	≥ 10⁵ MΩ, at 25°C with rated voltage applied.
Rated Voltage (WVDC)	See capacitance table.
Dielectric Withstanding Voltage (DWV)	Apply 250% of rated voltage for 5 seconds.
Operating Temperature Range	-55°C ~ +150°C (Contact Dalicap Technology Co., Ltd. if higher temperature is required.)
Temperature Coefficient (TC)	0 ± 30 ppm/°C
Capacitance Drift	±0.2% or ±0.05 pF, whichever is greater.
Piezoelectric Effect	None

Экологический эксперимент

Item	Specification	Method
Resistance to Soldering Heat	Appearance: No mechanical damage. Capacitance change: -1.0% ~ +2.0% or 0.5pF, whichever is greater. Q factor: Greater than 1000. Insulation resistance: Not less than the initial required value.	Preheat at 150°C ~ 180°C for 1 minute, immerse in solder at 260±5°C for 10±1 seconds. Test after cooling for 24±2 hours.
Thermal Shock	Appearance: No mechanical damage. Capacitance change: Not exceeding 0.5% or 0.5pF, whichever is greater. Q factor: Greater than 2000. Insulation resistance: Not less than 30% of the initial required value. DWV: Complies with the initial required value.	Test in accordance with MIL-STD-202, Method 107, Condition A. Expose at extreme temperatures for 15 minutes. Transition time from minimum to maximum operating temperature shall not exceed 5 minutes, for 5 cycles.
Moisture Resistance	Appearance: No mechanical damage. Capacitance change: Not exceeding 0.5% or 0.5pF, whichever is greater. Q factor: Greater than 300. Insulation resistance: Not less than 30% of the initial required value. DWV: Complies with the initial required value.	Test in accordance with MIL-STD-202, Method 106.
Steady State Humidity	Appearance: No mechanical damage. Capacitance change: Not exceeding 0.3% or 0.3pF, whichever is greater. Q factor: Greater than 300. Insulation resistance: Complies with the initial required value.	Test in accordance with MIL-STD-202, Method 103, Condition A. Apply 1.5V DC voltage under conditions of 85°C temperature and 85% humidity for 240 hours continuously.
Life	Appearance: No mechanical damage. Capacitance change: Not exceeding 2.0% or 0.5pF, whichever is greater. Q factor: Greater than 500. Insulation resistance: Not less than 30% of the initial required value.	Test in accordance with MIL-STD-202, Method 108. Apply 2 times the rated voltage at the extreme temperature for 2000 hours.

Кривая производительности DLC75N

На кривой S21 конденсатора имеется несколько параллельных точек резонанса (V-образных точек затухания). Первая частота параллельного резонанса FPR представляет собой частоту самой низкой точки параллельного резонанса. На него не влияют толщина подложки и диэлектрическая проницаемость, но влияет направление установки конденсатора. Горизонтальное направление означает, что внутренние электродные пластины конденсатора параллельны подложке.

На кривой входного сопротивления [Zin] конденсатора имеется несколько последовательных резонансных точек (V-образных точек затухания). Резонансная частота первого ряда FSR — это частота самой низкой резонансной точки ряда. В этот момент мнимая часть входного сопротивления Im[Zin] равна нулю (Im[Zin] = 0). Ниже FSR действительная часть Re[Zin] и мнимая часть Im[Zin] входного импеданса не изменяются линейно с частотой. Размер FSR связан со следующими факторами: структурой внутренних электродов конденсатора, материалом подложки, толщиной подложки, диэлектрической проницаемостью подложки, направлением установки конденсатора на подложку и размером площадок подложки.

Условия определения и измерения:

Определение: Конденсатор подключен последовательно к микрополосковой линии. То есть конденсатор замыкается между двумя концами микрополосковой линии сопротивлением 50 Ом через зазор. Условия измерения: подложка Ro3006 Rogers с диэлектрической проницаемостью 6,15, толщина подложки, установленная горизонтально, равна 10 мил, зазор микрополоски составляет 6 мил, а ширина микрополоски составляет 14,1 мил. Базовая плоскость находится на краю образца. Все данные взяты из электрической модели, созданной Modelithics Inc., которая основана на большом объеме данных измерений на различных подложках.